Effects of thermomechanical history on the tensile behavior of nitinol ribbon

Shape memory alloys (SMAs) have enormous potential for a wide variety of applications. A large body of work exists on the characterization of the microstructure and stress-strain behavior of these alloys, Nitinol (NiTi) in particular. However, many attributes of these materials are yet to be fully understood. Previous work at NASA Langley Research Center (LaRC) has included fabrication of hybrid composite specimens with embedded Nitinol actuators and modeling of their thermomechanical behavior. An intensive characterization effort has been undertaken to facilitate fundamental understanding of this alloy and to promote implementation of Nitinol in aerospace applications. Previous work revealed attributes of the Nitinol ribbon that were not easily rationalized with existing data in the literature. In particular, tensile behavior at ambient temperature showed significant dependence on the thermomechanical history prior to testing. The present work is focused on characterizing differences in the microstructure of Nitinol ribbons exposed to four different thermomechanical histories and correlation of the microstructure with tensile properties. Differential scanning calorimetry (DSC) and x-ray diffraction (XRD) analysis were employed to rationalize the microstructures present after exposure to various thermomechanical histories. Three of the Nitinol ribbon conditions were reversible upon heating (in the DSC) through the reverse transformation temperature (A(sub f) to transform the microstructure to austenite. However, the prior thermomechanical conditioning for the Nitinol ribbon that reflected the entire fabrication procedure (4% thermal cycle condition) was found to have an irreversible effect on the microstructure, as it remained unchanged after repeated complete thermal cycles. Tensile tests were conducted to determine the effect of prior thermomechancal conditioning on both the tensile behavior of the Nitinol ribbons and the stress state of the microstructure. The stress-strain behavior of the Nitinol actuators appears to be governed by the interplay between two major variables: namely, microstructural constituents such as the R-phase and the martensite; and the stress state of these constituents (whether twinned with low residual stresses, or detwinned with high residual stresses). The most significant difference in the stress-strain behavior of the four conditions, the critical stress required to achieve an initial stress plateau, was found to depend on b