Effect of the crystalline texture upon the properties of the permanent SmCo5 magnets

An X‐ray analysis of the crystal texture in sintered SmCo5 magnets is carried out serving as a basis for determination of magnetization curves within the framework of the single‐domain axially‐aligned particles. A comparison of the theoretical curves with those obtained experimentally in fields up to 65 kOe within the temperature range from 4 to 293 K reveales the ability of the model to explain the curves obtained on reducing the field down to zero. By varying the values of the anisotropy field HA as well as the specific magnetization σs when calculating the magnetization curves and their comparison with the experimental ones, the temperature dependence for HA and σs is determined within the framework of the present model. A series of characteristic features of the magnetization process in the materials under study is shown to be caused by the imperfection of the texture. Eine Röntgenanalyse der Kristalltextur in gesinterten SmCo5‐Magneten wird als Grundlage für die Bestimmung der Magnetisierungskurven im Rahmen axial‐ausgerichteter Ein‐Domänen‐Teilchen durchgeführt. Ein Vergleich der theoretischen Kurven mit experimentellen Kurven bei Feldern bis zu 65 kOe im Temperaturbereich von 4 bis 293 K zeigt, daß das Modell in der Lage ist, Kurven zu erklären, die bei Verringerung des Feldes bis auf Null erhalten werden. Bei der Berechnung der Magnetisierungskurven und ihrem Vergleich mit den experimentellen Kurven wird durch Variation sowohl der Werte des Anisotropiefeldes HA als auch der spezifischen Magnetisierung σs die Temperaturabhängigkeit für HA und σs im Rahmen des vorliegenden Modells bestimmt. Es wird gezeigt, daß eine Reihe von charakteristischen Einzelheiten des Magnetisierungsprozesses in den untersuchten Materialien durch die Fehler der Textur verursacht werden.