Effect of bone density and cement morphology on biomechanical stability of tibial unicompartmental knee arthroplasty

Unicompartmental knee arthroplasty (UKA) offers good long-term survivorship and superior kinematics and function compared with total knee arthroplasty (TKA). However, revision rates are higher with aseptic loosening representing a major cause. Biomechanical stability depends on cement penetration. The goal of this study was to analyze the influence of cement morphology and bone density on primary stability of tibial UKA under physiological loading conditions in human tibiae. Thirty-six tibial trays were implanted in fresh-frozen human cadaver knees and tested for primary stability using dynamic compression–shear testing. Prior to implantation, bone density had been quantified for all 18 tibiae. Postoperatively, cement penetration has been assessed on frontal cuts based on eight predefined parameters. The influence of bone density and cement morphology on biomechanical stability was determined using correlation and linear regression analysis. Mean failure load was 2691 ± 832.9 N, mean total cement thickness was 2.04 ± 0.37 mm, mean cement penetration was 1.54 ± 0.33 mm and mean trabecular bone mineral density (BMD) was 107.1 ± 29.3 mg/ml. There was no significant correlation between failure load and cement morphology (P > .05). Failure load was significantly positive correlated with trabecular BMD (r = 0.843; P