Results of apparent atomic oxygen reactions on Ag, C, and Os exposed during the Shuttle STS-4 orbits

Films selected for anticipated reaction with atomic oxygen, namely carbon, silver, and osmium, were exposed during the Shuttle STS-4 mission. A silver film within 5 nm of 225 nm thick was converted to a transparent blue-green interference film within 5 nm of 355 nm thick. Both carbon and osmium films 10-30 nm thick apparently formed volatile oxides and disappeared, except where well shielded. A calculated total of approximately 7 x 10 to the 19th oxygen atoms per sq cm struck the surfaces, which could have removed on the order of 3 microns of material if only 10 percent reacted. The absence of apparent effects on adjacent thin and thick gold films is offered as evidence that sputtering is not responsible.