Electromigration and residual resistivity of cobalt in gold

The electromigration of 57Co in gold is investigated by two methods (profile shift, steady‐state) at different temperatures. From this the effective charge of the gold matrix can be evaluated in good agreement with earlier results. Taking into account the vacancy flux effect the temperature dependence of the effective charge of Co in Au is given by zCoeff(T) = (1.1 ± 2.7) – (161 ± 30) μΩcm/ϱ resulting in a residual resistivity ϱd = (3.2 ± 0.6) μΩcm/at% of the thermally activated cobalt ions. Additionally performed resistivity measurements show a strong decrease of the atomic residual resistivity Δϱ (Co) with increasing temperature of cobalt atoms dissolved in gold. In the temperature range of the electromigration runs ϱd ≈ Δϱ(Co) is found. The experiments are compared to results of non‐transition metal impurities in gold. Der Elektrotransport von 57Co in Gold wird nach zwei Methoden (Profilverschiebung, stationärer Zustand) bei verschiedenen Temperaturen untersucht. Hieraus kann die effektive Ladung der Goldmatrix in guter Übereinstimmung mit früheren Ergebnissen bestimmt werden. Unter Berücksichtigung des Leerstellenflußeffektes ergibt sich für die Temperaturabhängigkeit der effektiven Ladung von Co in Au zCoeff(T) = (1,1 ± 2,7) – (161 ± 30) μΩcm/ϱ mit einem Zusatzwiderstand ϱd = (3,2 + 0,6) μΩcm/At% für die thermisch aktivierten Kobaltionen. Zusätzlich durchgeführte Widerstandsmessungen zeigen eine starke Abnahme des atomaren Zusatzwiderstands der in der Goldmatrix gelösten Kobaltatome mit wachsender Temperatur. Im Temperaturbereich der Elektrotransportexperimente erhält man ϱd ≈ Δϱ(Co). Die Experimente werden verglichen mit Ergebnissen von Nicht‐Übergangsmetallfremdatomen in Gold.