A technique for eliminating the undesirable effect of enhanced anodic corrosion of installations connected to anodically protected equipment

Two techniques for eliminating the unsiderable effect of anodic protection on installations connected to the protected equipment were tested. Model measurements were carried out in a 50% solution of sulfuric acid at 20°C with a type FeCr 18 Ni9 Ti stainless steel under potentiostatic conditions. The use of an insulating section in the critical range of potentials in the case of tubing passivation does not fully eliminate the increased corrosion due to anodic protection of a major piece of equipment. However, the undesirable effect can be eliminated entirely by installing secondary electrodes which pass electric current so as to set up the desired drop of potential. Methode zur Eliminierung der verstärkten anodischen Korrosion von mit anodisch geschützten Apparaten verbundenen Anlagen Zwei Methoden zur Eliminierung des ungünstigen Einflusses von anodischem Schutz auf mit diesen Apparaturen verbundenen Anlagen werden untersucht; dabei werden mit einem Stahl des Typs Cr 18 9 NiTi in 50%iger Schwefelsäure bis 20°C Modellmessungen unter potentiostatischen Bedingungen durchgeführt. Die Verwendung eines isolierenden Abschnitts im kritischen Potentialbereich bei der Passivierung von Rohren führt nicht zur Ausschaltung der verstärkten Korrosion, die durch den anodischen Schutz einer größeren Apparatur bedingt ist. Vollkommen ausschalten lässt sich der negative Effekt hingegen durch Sekundärelektroden, die einen elektrischen Strom liefern, so daß der gewünschte Potentialabfall erreicht wird.