Crystallisation Temperature of Amorphous Fe sub 80B sub 20 Under Pressure
The crystallisation temp. of Fe sub 80B sub 20 was measured as a of pressure at a heating rate of 7 deg K/min. The temp. increased with a of about 15 deg K/GPa. The crystallisation temp. was determined as a of heating rate at atmospheric pressure and compared with other results for the same glass. T...
Gespeichert in:
| Veröffentlicht in: | Journal of non-crystalline solids 1978-10, Vol.30 (1), p.69-76 |
|---|---|
| Hauptverfasser: | , |
| Format: | Artikel |
| Sprache: | eng |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Zusammenfassung: | The crystallisation temp. of Fe sub 80B sub 20 was measured as a of pressure at a heating rate of 7 deg K/min. The temp. increased with a of about 15 deg K/GPa. The crystallisation temp. was determined as a of heating rate at atmospheric pressure and compared with other results for the same glass. There were significant differences between glasses of the nominal composition but with different origin. 9 ref.--M.G.S. |
|---|---|
| ISSN: | 0022-3093 |