Microcrystalline cellulose from Posidonia oceanica brown algae: Extraction and characterization

Posidonia oceanica brown algae (POBA) represent an abundant and renewable biomass in Algerian seas. In the present study, the POBA were chemically treated through delignification and alkali treatment followed by acid hydrolysis to produce pure microcrystalline cellulose (MCC). FTIR analysis indicates that most lignin and hemicellulose were eliminated during the chemical treatments. The XRD measurements revealed that the obtained cellulose and MCC belong to cellulose I polymorph, with crystallinity index of 60.50% and 74.23%, respectively. SEM micrographs of the produced MCC showed a non-uniform micro sized rod-like shape morphology with an average diameter of 8.4 ± 2.1 μm. The thermal analysis results exhibited that the decomposition temperature of the prepared MCC shifted to higher temperature compared to that of the respective cellulose and raw POBA. The authenticity of the prepared MCC was also examined by comparing its physicochemical properties with those of commercial MCC. Based on these analyses, POBA-MCC showed tremendous potential to be used in several applications.