Synthesis, Characterization and Drug Loading of Multiresponsive pNIPAm-co-PEGMA (core)/pNIPAm-co-AAc (Shell) Nanogels with Monodisperse Size Distributions

We report the synthesis and properties of temperature- and pH-responsive p([NIPAm-co-PEGMA] (core)/[NIPAm-co-AAc] (shell)) nanogels with narrow size distributions, tunable sizes and increased drug loading efficiencies. The core-shell nanogels were synthesized using an optimized two-stage seeded polymerization methodology. The core-shell nanogels show a narrow size distribution and controllable physico-chemical properties. The hydrodynamic sizes, charge distributions, temperature-induced volume phase transition behaviors, pH-responsive behaviors and drug loading capabilities of the core-shell nanogels were investigated using transmission electron microscopy, zeta potential measurements, dynamic light scattering and UV-Vis spectroscopy. The size of the core-shell nanogels was controlled by polymerizing NIPAm with crosslinker poly(ethylene glycol) dimethacrylate (PEGDMA) of different molecular weights (Mn-200, 400, 550 and 750 g/mol) during the core synthesis. It was found that the swelling/deswelling kinetics of the nanogels was sharp and reversible; with its volume phase transition temperature in the range of 40⁻42 °C. Furthermore, the nanogels loaded with l-3,4-dihydroxyphenylalanine (L-DOPA), using a modified breathing-in mechanism, showed high loading and encapsulation efficiencies, providing potential possibilities of such nanogels for biomedical applications.We report the synthesis and properties of temperature- and pH-responsive p([NIPAm-co-PEGMA] (core)/[NIPAm-co-AAc] (shell)) nanogels with narrow size distributions, tunable sizes and increased drug loading efficiencies. The core-shell nanogels were synthesized using an optimized two-stage seeded polymerization methodology. The core-shell nanogels show a narrow size distribution and controllable physico-chemical properties. The hydrodynamic sizes, charge distributions, temperature-induced volume phase transition behaviors, pH-responsive behaviors and drug loading capabilities of the core-shell nanogels were investigated using transmission electron microscopy, zeta potential measurements, dynamic light scattering and UV-Vis spectroscopy. The size of the core-shell nanogels was controlled by polymerizing NIPAm with crosslinker poly(ethylene glycol) dimethacrylate (PEGDMA) of different molecular weights (Mn-200, 400, 550 and 750 g/mol) during the core synthesis. It was found that the swelling/deswelling kinetics of the nanogels was sharp and reversible; with its volume phase transition temperature in th