Effect of masticatory simulation on the translucency of different types of dental zirconia

Translucent zirconia has been marketed to dentists seeking to provide esthetic monolithic dental restorations. Evidence on differences in translucency between recently introduced translucent zirconia and conventional zirconia before and after fatigue testing with thermocycling is lacking. The purpose of this in vitro study was to evaluate the effect of fatiguing and thermocycling on the translucency of 5 mol% yttria partially stabilized zirconia (5Y-PSZ) and 3 mol% yttria partially stabilized zirconia (3Y-PSZ) at clinically relevant thicknesses. Translucent zirconia (BruxZir Anterior Solid Zirconia [5Y-PSZ]) and conventional zirconia (BruxZir Shaded Zirconia [3Y-PSZ]) were evaluated. Disk-shaped specimens were prepared to 0.7-mm and 1.2-mm thicknesses for each zirconia type. Four groups (n=10/group) were evaluated. Translucency parameter (TP), contrast ratio (CR), and light blockage percentage (Lb%) were recorded by using an integrating sphere spectrophotometer before and after fatiguing (1.2 million cycles at 110-N load with simultaneous thermocycling at 5 °C to 55 °C). Data were analyzed by repeated-measures analysis of variance for statistical significance (α=.05). CR values were compared with the reported 0.06 translucency perception threshold of the human eye. A statistically significant difference was found in TP, CR, and Lb% between 5Y-PSZ and 3Y-PSZ (P