Effect of Immediate Dentin Sealing on the Bond Strength of Monolithic Zirconia to Human Dentin

This study evaluated the shear bond strength (SBS) of pretreated monolithic zirconia surfaces bonded to human dentin following immediate dentin sealing (IDS) using two different self-adhesive resin luting agents. Sixty intact human third molars were collected, stored, sectioned appropriately, and molded according to ISO 29022:2013, resulting in 120 dentin specimens. Ceramic cylindrical specimens were fabricated using CAD/CAM technology and sintered as recommended (final bonding area A=2.56 mm ). Specimens were randomly assigned to eight groups (15≥n≥14) depending on dentin conditioning method (IDS or delayed dentin sealing [DDS]), zirconia surface pretreatment (airborne particle abrasion [APA] with 50 μm Al O particles at 3 bar for 10 seconds or tribochemical silica coating [TBC] with 30 μm CoJet particles at 2.8 bar for 10 seconds), and adhesive luting agent type (Panavia F2.0 [PAN] or PermaCem Dual Smartmix [PER]). Bonded specimens were water-stored (37°C, 24 hours) and subjected to SBS testing (50-kgF load cell, 1 mm/min). Fracture type was evaluated with stereomicroscopy. Data (MPa) were statistically analyzed using three-way analysis of variance (α=0.05). All factors significantly affected SBS values (