Hierarchical SnS2/CuInS2 Nanosheet Heterostructure Films Decorated with C60 for Remarkable Photoelectrochemical Water Splitting

Rational architectural design and catalyst components are beneficial to improve the photoelectrochemical (PEC) performance. Herein, hierarchical SnS2/CuInS2 nanosheet heterostructure porous films were fabricated and decorated with C60 to form photocathodes for PEC water reduction. Large-size CuInS2 nanosheet films were first grown on transparent conducting glass to form substrate films. Then, small-size SnS2 nanosheets were epitaxially grown on both sides of the CuInS2 nanosheets to form uniform hierarchical porous laminar films. The addition of C60 on the surface of the SnS2/CuInS2 porous nanosheets effectively increased visible light absorption of the composite photocathode. Photoluminescence spectroscopy and impedance spectroscopy analyses indicated that the formation of a SnS2/CuInS2 heterojunction and decoration of C60 significantly increased the photocurrent density by promoting the electron–hole separation and decreasing the resistance to the transport of charge carriers. The hierarchical SnS2/CuInS2 nanosheet heterostructure porous films containing multiscale nanosheets and pore configurations can enlarge the surface area and enhance visible light utilization. These beneficial factors make the optimized C60-decorated SnS2/CuInS2 photocathode exhibit much higher photocathodic current (4.51 mA cm–2 at applied potential −0.45 V vs reversible hydrogen electrode ) and stability than the individual CuInS2 (2.58 mA cm–2) and SnS2 (1.92 mA cm–2) nanosheet film photocathodes. This study not only reveals the promise of C60-decorated hierarchical SnS2/CuInS2 nanosheet heterostructure porous film photocathodes for efficient solar energy harvesting and conversion but also provides rational guidelines in designing high-efficiency photoelectrodes from earth-abundant and low-cost materials allowing widely practical applications.