Spin Configuration and Intrinsic Coercive Field of Narrow Domain Walls in Co5R-Compounds

In ferromagnetic materials with large anisotropy constants (K1 > 108 erg/cm3) the domain wall width, δB, is of the order of magnitude of a few lattice constants (10 to 30 Å). The spin configuration of such 180°‐walls in Co5R‐compounds is determined within the framework of the Heisenberg model. It is found that the deviations from the micromagnetic solution occur mainly in the centre of the wall. The wall energy was found to depend periodically on the position of the wall centre with respect to the crystal lattice. The oscillations of the wall energy give rise to a coercive field Hc = const (A/D) exp [– π δB/D] (A exchange constant, D wavelength perpendicular to the domain wall). The possibilities to obtain large intrinsic coercive fields are discussed in some detail. In ferromagnetischen Stoffen mit großer Kristallenergiekonstanten (K1 > 108 erg/cm3) beträgt die Blochwanddicke δB nur einige Atomabstände (10 bis 30Å). Die Spinverteilung einer 180°‐Bereichswand in den Co5R‐Verbindungen wird im Rahmen des Heisenberg‐modells berechnet. Es zeigt sich, daß Abweichungen von der mikromagnetischen Lösung hauptsächlich in der Wandmitte auftreten. In dünnen Wänden hängt die Wandenergie periodisch von der Position der Wandmitte bezüglich des Kristallgitters ab. Diese Schwankungen der Wandenergie haben eine Koerzitivfeldstärke Hc = const (A/D) exp [– π δB/D] zur Folge (A Austauschkonstante, D Wellenlänge senkrecht zur Wand). Die Möglichkeiten, auf diese Weise hohe Koerzitivfeldstärken zu erreichen, werden diskutiert.