Effect of Beam Profiles From Different Light Emission Tip Types of Multiwave Light-emitting Diodes on the Curing Profile of Resin-based Composites

Light activation is an important clinical step for achieving success in restorative procedures. This study evaluated the influence of beam profile from different light emission tip types of multiwave light-emitting diodes (LEDs) on the curing profile of resin-based composites. Experimental composites were produced containing either camphorquinone (CQ) or diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO) as a photoinitiator. Multiwave LEDs with either a bundle light guide tip (Bluephase G2, Ivoclar Vivadent) or a microlens tip (VALO Cordless, Ultradent) were characterized using a beam profiler. Block-shaped samples (5×5×3 mm depth) of the two composites were cured in a custom-designed mold with the multiwave LEDs positioned to compare the regions exposed to the 420-495 nm (blue) and 380-420 nm (violet) emittances. To map the curing profile, the degree of conversion (DC) of longitudinal thin cross sections from each block was evaluated using transmission FT-NIR. Radiant exposure transmitted through the composites during curing was evaluated at different thicknesses. Data were analyzed using analysis of variance and Tukey test (α=0.05; β=0.2). The results indicated that there were differences in the beam profile and the overall radiant exposures transmitted through the composites using each multiwave LED (