In vitro degradation of a unique porous PHBV scaffold manufactured using selective laser sintering

Biodegradable poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV) scaffolds have shown great promise for bone tissue engineering applications. The investigation of their hydrolytic degradation is thus essential to understand the effect of hydrolysis on the complex biodegradation behavior of PHBV sca...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of biomedical materials research. Part A 2019-01, Vol.107 (1), p.154-162
Hauptverfasser: Diermann, Sven H., Lu, Mingyuan, Edwards, Grant, Dargusch, Matthew, Huang, Han
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Biodegradable poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV) scaffolds have shown great promise for bone tissue engineering applications. The investigation of their hydrolytic degradation is thus essential to understand the effect of hydrolysis on the complex biodegradation behavior of PHBV scaffolds. In this study, we investigated the degradation behavior of high molecular weight PHBV scaffolds manufactured using selective laser sintering (SLS) without using predesigned porous architectures. The manufactured scaffolds have high specific surface areas with great water‐uptake abilities. After an incubation of 6 weeks in phosphate‐buffered saline solution, the structural integrity of the scaffolds was unaffected. However, a significant decrease in molecular weight ranging from 39% to 46% was found. The measured weight loss was negligible, but their compressive modulus and strength both decreased, likely due to water plasticization. These findings suggest that hydrolytic degradation of PHBV by means of bulk degradation was the predominant mechanism, attributed to their excellent water absorptivity. Overall, the PHBV scaffolds manufactured using SLS exhibited adequate mechanical properties and satisfactory structural integrity after incubation. As a result, the scaffolds have great potential as candidates for bone repair in clinical practice. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 107A: 154–162, 2019.
ISSN:1549-3296
1552-4965
DOI:10.1002/jbm.a.36543