Effect of silica-containing glass–ceramic liner treatment on zirconia coping retention

Zirconia prostheses show a high rate of retention loss, and more information is needed regarding the treatment of the intaglios of zirconia prostheses to improve the bond strength between zirconia and resin cement. The purpose of this in vitro study was to evaluate the retention of titanium abutment...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:The Journal of prosthetic dentistry 2018-11, Vol.120 (5), p.732-739
Hauptverfasser: Lee, Eun-Suk, Huh, Yoon-Hyuk, Park, Chan-Jin, Cho, Lee-Ra
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Zirconia prostheses show a high rate of retention loss, and more information is needed regarding the treatment of the intaglios of zirconia prostheses to improve the bond strength between zirconia and resin cement. The purpose of this in vitro study was to evaluate the retention of titanium abutments and zirconia prostheses treated with silica-containing glass–ceramic liners. The effect of the abutment convergence angle on retention force was also examined. Titanium abutments and zirconia copings (n=90) were fabricated with 3 different convergence angles (6, 12, and 24 degrees). Specimens were divided into 2 groups according to surface treatment: an airborne-particle-abraded control group and a group that was coated with a silica-containing glass–ceramic liner after airborne-particle abrasion (liner group). The thickness of the liner was measured, and the inner spacing of the zirconia coping was modified in the liner group. The coping was cemented, and the retention was evaluated with a tensile bond strength test by using a universal testing machine. Retention was analyzed by using a 2-way analysis of variance. Modes of failure were evaluated by examining the fracture surface. Elemental analysis of the interface was also performed. The liner group showed a significantly higher retention force for the zirconia prosthesis (P
ISSN:0022-3913
1097-6841
DOI:10.1016/j.prosdent.2017.12.005