Smart textile framework: Photochromic and fluorescent cellulosic fabric printed by strontium aluminate pigment

[Display omitted] •Photochromic cotton fabric is simply obtained by aqueous-based pigment-binder printing formulation containing inorganic pigment phosphor.•The printed layer on the fabric surface displays chameleon effects upon application of UV irradiation.•The printed fabric shows a reversible and rapid photochromic response during ultra-violet excitation without fatigue. Smart clothing can be defined as textiles that respond to a certain stimulus accompanied by a change in their properties. A specific class herein is the photochromic and fluorescent textiles that change color with light. A photochromic and fluorescent cotton fabric based on pigment printing is obtained. Such fabric is prepared by aqueous-based pigment-binder printing formulation containing inorganic pigment phosphor characterized by good photo- and thermal stability. It exhibits optimal excitation wavelength (365 nm) results in color and fluorescence change of the fabric surface. To prepare the transparent pigment-binder composite film, the phosphor pigment must be well-dispersed via physical immobilization without their aggregation. The pigment-binder paste is applied successfully onto cotton fabric using screen printing technique followed by thermal fixation. After screen-printing, a homogenous photochromic film is assembled on a cotton substrate surface, which represents substantial greenish-yellow color development as indicated by CIE Lab color space measurements under ultraviolet light, even at a pigment concentration of 0.08 wt% of the printing paste. The photochromic cotton fabric exhibit three excitation peaks at 272, 325 and 365 nm and three emission peaks at 418, 495 and 520 nm. The fluorescent optical microscope, scanning electron microscope, elemental mapping, energy dispersive X-ray spectroscopy, fluorescence emission and UV/Vis absorption spectroscopic data of the printed cotton fabric are described. The printed fabric showed a reversible and rapid photochromic response during ultra-violet excitation without fatigue. The fastness properties including washing, crocking, perspiration, sublimation/heat, and light are described.