Mechanical and Surface Properties of Monolithic Zirconia

This study compared monolithic zirconia with conventional ones based on mean roughness (Ra), Vickers hardness (VHN), topography, transmittance, grain size, flexural strength (FS), Weibull modulus, and fractographic behavior. One monolithic (Prettau Zircon [PR group]) and two conventional (ICE Zirkon Transluzent [IZ group] and BloomZir [BL group]) zirconias were used. Specimens were tested using a profilometer, a microhardness tester, a scanning electron microscope, a spectrophotometer, and a Universal Testing Machine (EMIC DL 2000). Ra, VHN, grain size, and transmittance were analyzed using the Kruskal-Wallis test associated with Dunn test (α=0.05). FS was analyzed using one-way analysis of variance with the Tukey honestly significant difference test (α=0.05). Means and standard deviations of roughness, after sintering (Ra, in μm) and VHN, were, respectively, 0.11 ± 0.01, 1452.16 ± 79.49, for the PR group; 0.12 ± 0.02, 1466.72 ± 91.76, for the IZ group; and 0.21 ± 0.08, 1516.06 ± 104.02, for the BL group. BL was statistically rougher ( p0.05). Weibull moduli were 12.47 for the PR group, 7.24 for the IZ group, and 6.31 for the BL group, with no statistical differences. The PR and BL groups had higher transmittance values and grain sizes than the IZ group ( p