Effect of coloring and sintering on the translucency and biaxial strength of monolithic zirconia

The influences of coloring and sintering procedures on the optical and mechanical properties of monolithic zirconia have not been thoroughly investigated. The purpose of this in vitro study was to investigate the effects of the coloring procedure and of varying final sintering temperatures on the translucency parameter (TP) and biaxial flexural strength (BFS) of monolithic zirconia. Disk-shaped specimens (N=210) of 2 different monolithic zirconia brands (Vita YZ HTWhite [VYZa]; Vita YZ HTColor A2 [VYZb]; Prettau Zirkonzahn [PZ]; Prettau Anterior Zirkonzahn [PZA]) with a diameter of 15 mm and a thickness of 1.0 ±0.05 mm were prepared. Half of the specimens prepared from noncolored blocks (VYZa, PZ, and PZA) received coloring liquid application. Then, the specimens were divided into 3 subgroups (n=10) according to the final sintering temperatures (1350°C, 1450°C, and 1600°C). The TP was determined by using a reflection spectrophotometer, and the BFS was tested with the piston-on-3-ball method in a universal testing machine. Data were statistically analyzed by multivariate multiple regression and Bonferroni tests (α=.05). Significant differences were obtained among the groups based on the results of the TP and BFS (P