Control of biodegradability of poly(3-hydroxybutyric acid) film with grafting acrylic acid and thermal remolding

Radiation‐induced graft polymerization of acrylic acid (AAc) on poly(3‐hydroxybutyric acid) (PHB) film was carried out and the resulting film was thermally‐remolded. The PHB films grafted with AAc (PHB‐g‐AAc) having a degree of grafting higher than 5% completely lost the enzymatic degradability. The enzymatic degradability of the grafted film was recovered by thermal remolding. The highest enzymatic degradation rate was observed at degree of grafting of 10% after thermal remolding. The PHB‐g‐AAc films and thermally‐remolded PHB‐g‐AAc films were characterized by contact angle and differential scanning calorimetry. The enzymatic degradability of PHB‐g‐AAc films was lost by the grafted AAc, which covered the surface of PHB film. The acceleration of enzymatic degradation in the remolded PHB‐g‐AAc films was mainly caused by decrease of crystallinity of PHB by dispread of grafted AAc during thermal remolding. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 3856–3861, 2006