Effect of microwave irradiation on carbon fiber/epoxy resin composite fabricated by vacuum assisted resin transfer molding

The effects of microwave irradiation for resin-curing of carbon fiber/epoxy resin composite (CFRTS), which was fabricated by vacuum-assisted resin transfer molding (VARTM) method, were investigated at 2.45 GHz frequency. The mechanical properties of CFRTS cured by microwave irradiation for 20 min at 120 °C were similar as compared to the conventional oven for 300 min at 120 °C. Moreover, the CFRTS irradiated by microwave had better adherence property between fiber and resin as compared to conventional oven at same resin-curing time. From the relation between resin-curing and mechanical property, it was found that the curing rate of microwave-irradiated CFRTS was 15 times faster as compared to conventional heating. Furthermore, the activation energies for resin-curing reaction on conventional- and microwave-cured CFRTS were estimated to be 2.7 and 1.3 × 10 4 J/mol, respectively. The resin-curing reaction in CFRTS prepared by VARTM method was significantly promoted by microwave irradiation at short time.