Effect of surface treatments on repair with composite resin of a partially monoclinic phase transformed yttrium-stabilized tetragonal zirconia

Abstract Statement of problem Studies of composite resin repairs of yttrium-tetragonal zirconia polycrystal (Y-TZP) are usually performed in its tetragonal phase, but it may be partially transformed into a monoclinic phase in a clinical fracture. Purpose The purpose of this in vitro study was to evaluate the effect of airborne-particle abrasion (APA) and a bonding agent on the shear bond strength (SBS) between a composite resin and hydrothermally aged Y-TZP. Material and methods Specimens (7.0×7.0×1.7 mm, N=112) of Y-TZP Lava were obtained, and 50% were aged in an autoclave at 134°C at 300 kPa for 8 hours. The surfaces were treated with APA 50-μm Al2 O3 particles (ALU) or Rocatec Soft (30 μm) (ROC) followed by Clearfil SE Bond Primer (10-methacryloyloxydecyl dihydrogen phosphate [10-MDP]) plus Clearfil porcelain bond activator (3-methacryloxypropyl-trimethoxy silane [3-MPS]) (CLE) or RelyX Ceramic Primer plus a layer of RelyX U100 adhesive-resin cement (REL). Composite resin cylinders were built on the Y-TZP treated surfaces. After thermal cycling (6000 cycles, 5°C and 55°C, 30-second dwell time), an SBS test was carried out (n=14). Data were analyzed by 3-way ANOVA and the Tukey honest significant differences test (α=.05). The failure mode was analyzed. Results The 3-way ANOVA was not significant for aging ( P >.05), but the APA ( P