Correspondence between Susceptibility to SCC of 7050 Aluminum Alloy and Passive Film-induced Stress at Various pH Values

The passive film-induced stress and the susceptibility to SCC of 7050 aluminum alloy in 3.5%sodium chloride solution at various pH values were investigated by slow strain rate testing（SSRT） and flowing stress differential method.The results showed that the passive film-induced stress and the susceptibility to SCC decreased with increasing pH values when pH≤7,while they increased with increasing pH values when pH7.However,the corrosion type was interpreted as exfoliation corrosion when pH=l and 14,and there was no film formed on the surface of the specimens.The whole variation plots of film-induced stress and the SCC susceptibility with pH values were both presented as a valley shape.The symbol and amount of the film-induced stress were related to the compositions of the passive film,which were analyzed using X-ray photoelectron spectroscopy（XPS）.