Indium selenide microrod films: chemical bath deposition from acidic bath

Indium selenide microrod films: chemical bath deposition from acidic bath

Films of indium selenide was deposited onto glass and indium tin oxide coated glass substrates in acidic medium using chemical bath deposition at room temperature. Indium sulphate and sodium selenosulphate were used as precursors of In 3+ and Se 2− , respectively. The structural, surface morphologic...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of materials science. Materials in electronics 2016-12, Vol.27 (12), p.12351-12356
Hauptverfasser: Bansode, Sanjay B., Kapadnis, Ramesh S., Ansari, Abu S., Wagh, Vasant G., Kulkarni, Anil N., Kale, Sampat S., Pathan, Habib M.
Format: Artikel
Sprache:eng
Schlagworte:
Characterization and Evaluation of Materials
Chemistry and Materials Science
Deposition
Diffraction
Evolution
Glass
Indium selenides
Indium sulfate
Materials Science
Optical and Electronic Materials
Optical properties
Sodium
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Films of indium selenide was deposited onto glass and indium tin oxide coated glass substrates in acidic medium using chemical bath deposition at room temperature. Indium sulphate and sodium selenosulphate were used as precursors of In 3+ and Se 2− , respectively. The structural, surface morphological and optical properties of the deposited films were studied. Diffractograms in structural study revealed the deposited material is In 2 Se 3 films. Controlled bath conditions resulted in the evolution of the In 2 Se 3 microrod-like morphology. The optical band gap of the film was found to be 1.7 eV.
ISSN:0957-4522
1573-482X
DOI:10.1007/s10854-016-5145-6