"Smart poisoning" of Co/SiO2 catalysts by sulfidation for chirality-selective synthesis of (9,8) single-walled carbon nanotubes

The chirality-selective synthesis of relatively large (diameter > 1 nm) single-walled carbon nanotubes (SWCNTs) is of great interest for a variety of practical applications, but only a few catalysts are available so far. Previous studies suggested that S (compounds) can enhance the chirality-selectivity of Co catalysts in SWCNT synthesis, however, the mechanism behind is not fully understood, and no tailorable methodology has yet been developed. Here, we demonstrate a facile approach to achieve the chirality-selective synthesis of SWCNTs by the sulfidation-based poisoning of silica-supported Co catalysts using a mixture of H2S and H2. The UV-vis-NIR, photoluminescence, and Raman spectroscopy results together show that the resulting SWCNTs have a narrow diameter distribution of around 1.2 nm, and (9,8) nanotubes have an abundance of similar to 38% among the semiconducting species. More importantly, the carbon yield achieved by the sulfided catalyst (2.5 wt%) is similar to that of the nonsulfided one (2.7 wt%). The characterization of the catalysts by X-ray diffraction, X-ray photoelectron spectroscopy, X-ray fluorescence, and H2 temperature-programmed reduction shows that the sulfidation leads to the formation of Co9S8 nanoparticles. However, Co9S8 nanoparticles are reduced back to regenerate metallic Co nanoparticles during the synthesis of SWCNTs, which maintain a high carbon yield. In this process, Co9S8 nanoparticles seemingly intermediate the production of Co nanoparticles with narrow size distribution. Due to the fact that the poisoning step improves the quality of the end-product rather than hampering the growth process, we have coined the process developed as "smart poisoning". This study not only reveals the mechanism behind the beneficial role of S in the selective synthesis of relatively large SWCNTs but also presents a promising method to create chirality-selective catalysts with high activity for scalable synthesis.