Effect of Mixed-Phase TiO sub(2)/PVA Nanofibers on the Degradation on Methyl Orange

We report on the synthesis of nanostructured TiO sub(2) for various structural phases and observed the rate of degradation of methyl orange (MO) upon UV irradiation. Mixed phase nanocrystalline TiO sub(2) at temperature of 800[degrees]C shows higher rate of degradation of MO with the rate of 0.0203/min compared to other phases. This rate corresponds to the percentage of MO degradation of 58.85%, 71.69%, 86.25% and 91.82% for duration of 30, 60, 90 and 120 min of UV irradiations, respectively. The TiO sub(2) powder was prepared using titanium (IV) butoxide as the precursor via sol gel process. The samples were characterized using X-ray diffractometer (XRD) and field emission scanning electron microscopy (FESEM). The rate of degradation of MO after UV exposure was measured using UV-Vis spectrophotometer. The first order reaction rate constants (k sub(a)pp of anatase; mixed-phase; and rutile phases were 0.0130, 0.0203 and 0.0029, respectively, which shows that mixed-phase TiO sub(2) has higher k sub(a)ppvalue indicating higher rate of degradation. The PVA/TiO sub(2) nanofibers were produced via electrospinning technique and similar tests on the nanofibers were conducted.Energy dispersive X-ray spectroscopy (EDX) indicates significant presence of TiO sub(2) is in nanofibers and the average diameter of the nanofibers was 600 nm.