β-Mn formation and aging effect on the fracture behavior of high-Mn low-density steels
The β-Mn formation behavior of high-Mn low-density steels was investigated in terms of the morphological characteristics and alloying element distribution after aging treatments. A dramatic difference in the formation kinetics and morphology of β-Mn was observed depending on the addition of Al, whic...
Gespeichert in:
Veröffentlicht in: | Scripta materialia 2016-11, Vol.124, p.193-197 |
---|---|
Hauptverfasser: | , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The β-Mn formation behavior of high-Mn low-density steels was investigated in terms of the morphological characteristics and alloying element distribution after aging treatments. A dramatic difference in the formation kinetics and morphology of β-Mn was observed depending on the addition of Al, which may increase the driving force for β-Mn formation. In addition, the effects of the aging process on the fracture behavior were examined in uniaxial tensile tests combined with microstructural observations. A severe loss of ductility resulted from the β-Mn formation and ordering of ferrite into the D03 phase, which was transformed before the β-Mn formation process. |
---|---|
ISSN: | 1359-6462 1872-8456 |
DOI: | 10.1016/j.scriptamat.2016.04.040 |