Effect of solvent/disinfectant ethanol on the micro-surface structure and properties of multiphase denture base polymers
The aim of this study was to evaluate the effect of solvent/disinfectant ethanol on the surface of denture base polymers. Changes in surface roughness, topography and some nanomechanical properties were assessed by SEM and nanoindentation plotted against different concentrations of ethanol on heat c...
Gespeichert in:
Veröffentlicht in: | Journal of the mechanical behavior of biomedical materials 2016-02, Vol.54, p.1-7 |
---|---|
Hauptverfasser: | , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The aim of this study was to evaluate the effect of solvent/disinfectant ethanol on the surface of denture base polymers. Changes in surface roughness, topography and some nanomechanical properties were assessed by SEM and nanoindentation plotted against different concentrations of ethanol on heat cured and autopolymerized polymetyl methacrylate based acrylic denture base polymers.
Test specimens (10×10×3mm3) of heat-curing (HC) and auto-polymerizing (AP) acrylic resin were prepared and polished to obtain uniform smoothness which were further grouped into 3 sub-groups HC1, HC2, HC3 and AP1, AP2, AP3 respectively 10 specimens (n) in each group. HC1 and AP1, HC2 and AP2, HC3 and AP3 were treated with 99.9%, 70% and 40% respectively for 30, 60 and 120s followed by analysis of surface roughness (Sa), topographical changes and some nanomechanical properties.
Both HC and AP resins showed changes in their Sa and nanomechanically measured modulus of elasticity and surface hardness after being treated at different concentrations of ethanol and at different lengths of time. Surface changes were most clearly seen in autopolymerizing denture base polymer, especially at the interface region between the PMMA polymer bead and polymer matrix. There was a correlation (R2=0.83, r=0.91, P |
---|---|