Preparation, characterization and properties of nano-hydroxyapatite/polypropylene carbonate biocomposite

The combination of nano-hydroxyapatite (n-HA) and polypropylene carbonate (PPC) was used to make a composite materials by a coprecipitation method. The physical and chemical properties of the composite were tested. Scanning electron microscope (SEM) observation indicated that the biomimetic n-HA cry...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Materials Science & Engineering C 2016-06, Vol.63, p.285-291
Hauptverfasser: Liao, Jianguo, Li, Yanqun, Zou, Qin, Duan, Xingze, Yang, Zhengpeng, Xie, Yufen, Liu, Haohuai
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The combination of nano-hydroxyapatite (n-HA) and polypropylene carbonate (PPC) was used to make a composite materials by a coprecipitation method. The physical and chemical properties of the composite were tested. Scanning electron microscope (SEM) observation indicated that the biomimetic n-HA crystals were uniformly distributed in the polymer matrix. As the n-HA content increased in the composite, the fracture mechanism of the composites changes from gliding fracture to gliding and brittle fracture. Furthermore, the chemical interaction between inorganic n-HA and polypropylene carbonate was also investigated and discussed in detail. The hydrogen bonds might be formed between –OH/CO32− of n-HA crystal and the ester group (–COO–) of PPC. The tensile strength of n-HA/PPC (40/60) was similar to that of the cancellous bone, and reached ca 58MPa. The osteoblasts were cultured for up to 7days, and then the adhesion and proliferation of osteoblasts were measured by Methyl thiazolyl tetrazolium (MTT) colorimetry assay and SEM. The cells proliferated, grew normally in fusiform shape and well attached. The in vitro test confirmed that the n-HA/PPC composites were biocompatible and showed undetectable negative effect on osteoblasts. In vivo implantation of the composite in New Zealand white rabbits was performed. It can stimulate the growth of a new bone, and at the same time the material begins to degrade. These results suggested that the composite may be suitable for the reparation or replacement of bone defects and possessed the potential for clinical applications. SEM micrographs of the induced osteoblasts cultured on the n-HA/PC (40/60) composite. After 2day cell culture (a), after 4days (b) hematoxylin/eosin-stained sections of n-HA/PPC (40/60) composite materials. In the photos, M denotes n-HA/PPC (40/60) composite materials, B denotes bone, while NB denotes newly formed bone tissue. [Display omitted] •A novel method, co-solution, coprecipitation and dehydrated ethanol treatment is employed for n-HA/PPC biomaterial.•PEG6000 was modified on n-HA surface to create chemical bondings between the inorganic mineral and organic polymer.•n-HA is distributed evenly in the PPC matrix, and good interface bonding between n-HA and PPC is observed.•The in vivo test confirms that the n-HA/PPC composite is biocompatible and shows no negative effect on osteoblasts.