Control of Interpenetration and Gas-Sorption Properties of Metal-Organic Frameworks by a Simple Change in Ligand Design

In metal–organic framework (MOF) chemistry, interpenetration greatly affects the gas‐sorption properties. However, there is a lack of a systematic study on how to control the interpenetration and whether the interpenetration enhances gas uptake capacities or not. Herein, we report an example of interpenetration that is simply controlled by the presence of a carbon–carbon double or single bond in identical organic building blocks, and provide a comparison of gas‐sorption properties for these similar frameworks, which differ only in their degree of interpenetration. Noninterpenetrated (SNU‐70) and doubly interpenetrated (SNU‐71) cubic nets were prepared by a solvothermal reaction of [Zn(NO3)2]⋅6 H2O in N,N‐diethylformamide (DEF) with 4‐(2‐carboxyvinyl)benzoic acid and 4‐(2‐carboxyethyl)benzoic acid, respectively. They have almost‐identical structures, but the noninterpenetrated framework has a much bigger pore size (ca. 9.0×9.0 Å) than the interpenetrated framework (ca. 2.5×2.5 Å). Activation of the MOFs by using supercritical CO2 gave SNU‐70′ and SNU‐71′. The simulation of the PXRD pattern of SNU‐71′ indicates the rearrangement of the interpenetrated networks on guest removal, which increases pore size. SNU‐70′ has a Brunauer–Emmett–Teller (BET) surface area of 5290 m2 g−1, which is the highest value reported to date for a MOF with a cubic‐net structure, whereas SNU‐71′ has a BET surface area of 1770 m2 g−1. In general, noninterpenetrated SNU‐70′ exhibits much higher gas‐adsorption capacities than interpenetrated SNU‐71′ at high pressures, regardless of the temperature. However, at P