Effect of post weld heat treatment on the microstructure and tensile properties of activated flux TIG welds of Inconel X750

This study addresses the effect of post weld heat treatment on the fusion zone microstructure and the mechanical properties of activated flux tungsten inert gas (A-TIG) weldments of Inconel X750. In this study, a compound flux of 50% SiO2+50% MoO3 was used for A-TIG welding of the samples. Comparative studies on the microstructure and mechanical properties have been made on the weldments both in the as-welded and post weld heat treated conditions. Direct ageing post weld heat treatment (PWHT) was carried out at 705°C for 22h on the A-TIG weldment to assess the structure–property relationships. It was inferred that direct ageing post weld heat treatment resulted in better tensile strength (1142MPa) compared to the as-welded coupons (736MPa). The joint efficiencies of the as-welded and post weld heat treated conditions were found to be 60.7% and 94.07% respectively. The impact toughness of the as-welded coupons were found to be greater than the post weld heat treated samples; however the impact toughness of the welds are greater than the parent metal employed in both the cases. This study also attested the detailed structure–property relationships of A-TIG weldments using the combined techniques of optical and scanning electron microscopy, Electron Dispersive X-ray Analysis (EDAX) techniques.