Cladding of Advanced Al Alloys Employing Friction Stir Welding

Friction stir welding (FSW) is a relatively new solid-state joining technology for metals. It shows no solidification-related joint imperfections which makes it utmost suitable for hard-to-weld highly alloyed aerospace aluminium grades, like AA 2xxx and AA 7xxx. These alloys are often cladded with a thin layer of pure aluminium for corrosion protection. Friction stir welding of such materials requires removal of the clad layer prior to welding to prevent weakening of the joint by the soft clad material. This leaves the welded region vulnerable to corrosion after the joining process. Post-weld restoration of the clad layer is required to restore the protective action of the clad layer and as such to enhance the life expectancy of the welded construction. In this work the deposition of thin layers of pure aluminium on AA 2xxx and AA 7xxx alloys is studied employing an innovative FSW tool. The tool shoulder is equipped with strategically placed internal channels that allow delivery of filler type of material into the weld zone. Depending on the channel architecture used, filler material can be deposited on top of the work piece surface and/or mixed with the work piece surface region. The cladding is done in the solid state avoiding many problems with solidification and interface reactivity often observed with other surface modification techniques, such as laser surface engineering, plasma spraying or casting. Here, the filler material is deposited on top of the work piece; the modified tool is not equipped with a tool pin. The work comprises an in depth study of the influence of process conditions on the microstructural changes in the underlying work piece and on the quality of the bonding of the clad material (99.5 % aluminium) to the work piece material. Apart from the usual process conditions, such as tool rotation speed, translation speed, down force and tool angle also the delivery pressure and rate of the filler supply system can be varied. The influence of the usual process conditions on the microstructure of the underlying work piece is similar to that observed with “traditional” FSW. Changes in hardness can be related to the amount of heat generated by the welding process. Shape and dimensions of the microstructural zones found are typical for welds made without a tool pin. The effect of the small amount of clad material deposited on top of the work piece on the temperature distribution is small. The amount of heat required to heat it up is negligibl