Formation of the Spinel Phase in the Layered Composite Cathode Used in Li-Ion Batteries

Pristine Li-rich layered cathodes, such as Li1.2Ni0.2Mn0.6O2 and Li1.2Ni0.1Mn0.525Co0.175O2, were identified to exist in two different structures: LiMO2 R3̅m and Li2MO3 C2/m phases. Upon 300 cycles of charge/discharge, both phases gradually transform to the spinel structure. The transition from LiMO...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:ACS Nano, 7(1):760-767 7(1):760-767, 2013-01, Vol.7 (1), p.760-767
Hauptverfasser: Gu, Meng, Belharouak, Ilias, Zheng, Jianming, Wu, Huiming, Xiao, Jie, Genc, Arda, Amine, Khalil, Thevuthasan, Suntharampillai, Baer, Donald R, Zhang, Ji-Guang, Browning, Nigel D, Liu, Jun, Wang, Chongmin
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Pristine Li-rich layered cathodes, such as Li1.2Ni0.2Mn0.6O2 and Li1.2Ni0.1Mn0.525Co0.175O2, were identified to exist in two different structures: LiMO2 R3̅m and Li2MO3 C2/m phases. Upon 300 cycles of charge/discharge, both phases gradually transform to the spinel structure. The transition from LiMO2 R3̅m to spinel is accomplished through the migration of transition metal ions to the Li site without breaking down the lattice, leading to the formation of mosaic structured spinel grains within the parent particle. In contrast, transition from Li2MO3 C2/m to spinel involves removal of Li+ and O2‑, which produces large lattice strain and leads to the breakdown of the parent lattice. The newly formed spinel grains show random orientation within the same particle. Cracks and pores were also noticed within some layered nanoparticles after cycling, which is believed to be the consequence of the lattice breakdown and vacancy condensation upon removal of lithium ions. The AlF3-coating can partially relieve the spinel formation in the layered structure during cycling, resulting in a slower capacity decay. However, the AlF3-coating on the layered structure cannot ultimately stop the spinel formation. The observation of structure transition characteristics discussed in this paper provides direct explanation for the observed gradual capacity loss and poor rate performance of the layered composite. It also provides clues about how to improve the materials structure in order to improve electrochemical performance.