Fabrication of nano-structure anti-reflective lens using platinum nanoparticles in injection moulding

We provide a lens mould to attain an anti-reflection sub-wavelength structure (SWS) for plastic replica in the injection moulding process. To obtain the SWS on the lens mould, platinum nanoparticles formed by decomposition of a platinum oxide were employed. The fabricated platinum nanoparticles were estimated to be 90 nm in diameter, on average, and the dispersion of the particle diameter was evaluated to be 20 nm. Through nanostructure replication by injection moulding, antireflection of less than 0.5% was achieved, and transmittance increased over 98%. In addition, a high-replication durability of over 10 000 times was attained. The variation of the minimum reflection ratio was evaluated to be 0.38% 0.04%. The usefulness of the proposed SWS mould for mass-production was confirmed, as it allows for high durability and SWS formation on the lens surface.