Magnetization reversal in Co zigzag nanocolumns grown by glancing angle deposition
A Co zigzag nanocolumn sample was grown by glancing angle deposition using molecular beam epitaxy. A structural study was carried out using scanning electron microscopy and the magnetic properties and the magnetoresistance were investigated at room temperature. Each zigzag consisted of six arms tilt...
Gespeichert in:
Veröffentlicht in: | Thin solid films 2014-10, Vol.568, p.13-18 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | A Co zigzag nanocolumn sample was grown by glancing angle deposition using molecular beam epitaxy. A structural study was carried out using scanning electron microscopy and the magnetic properties and the magnetoresistance were investigated at room temperature. Each zigzag consisted of six arms tilted with respect to each other by approx. 60°, had a club-like shape, diameter in the range of 20–100nm, a single arm length of about 150nm and a total height of approx. 370nm. The magnetization hard axis was observed for the magnetic field oriented parallel to the zigzag long axis and the easy axis for the field oriented perpendicular to the long axis. The system exhibited very high maximum coercivity values, which could find potential applications. The angular dependences of the coercive field and the remanent to saturation magnetization ratio, as well as magnetoresistance curves, indicated the presence of curling magnetization reversal mode.
•Cobalt zigzag nanocolumns were grown by glancing angle deposition.•The structure and the magnetic properties of the columns were studied.•The system exhibited high max. Hc values which could find potential applications.•The results indicated the presence of curling magnetization reversal mode. |
---|---|