Microstructures and mechanical properties of SiCp/AZ91 magnesium matrix nanocomposites processed by multidirectional forging

•As-cast SiCp/AZ91 nanocomposite was subjected to multidirectional forging.•Ultrafine grains with average size of about 20nm were observed.•Tensile properties was significantly improved after 6 MDF passes. A particulate reinforced magnesium matrix nanocomposite was subjected to multidirectional forging (MDF). The results showed that the microstructure of the nanocomposite mainly consisted of some large initial grains and fine recrystallized grains along initial grain boundaries after 1 MDF pass. With increasing the MDF passes, the degree of dynamic recrystallization increased and ultrafine grains with average size of about 20nm were observed in the nanocomposites after 6 MDF passes. The distribution of SiC nanoparticles in the nanocomposite was homogeneous outside some SiC nanoparticle dense zones after different MDF passes. Compared with typical basal texture obtained for 1 MDF pass, the basal pole intensity decreased firstly for 3 MDF pass and then increased for 6 MDF passes. Both ultimate tensile strength and elongation to fracture of the nanocomposite were enhanced with increasing the MDF passes, while yield strength decreased after 3 MDF passes and then increased slightly after 6 MDF passes.