Superior magnetic softness at elevated temperature of Si-rich Fe-based nanocrystalline alloy
An excellent high-temperature magnetic softness was observed in a Si-rich nanocrystalline Fe74.5Cu1Nb2Si17.5B5 alloy. The Curie temperatures of amorphous and crystal phases, TCA* and TCcry, for this alloy were detected to be 365 °C and 580 °C, respectively. For the 480 °C-annealed alloy, the initial...
Gespeichert in:
Veröffentlicht in: | Journal of applied physics 2012-10, Vol.112 (8) |
---|---|
Hauptverfasser: | , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | An excellent high-temperature magnetic softness was observed in a Si-rich nanocrystalline Fe74.5Cu1Nb2Si17.5B5 alloy. The Curie temperatures of amorphous and crystal phases, TCA* and TCcry, for this alloy were detected to be 365 °C and 580 °C, respectively. For the 480 °C-annealed alloy, the initial permeability μi drops to nearly zero just above TCA*; however, for the 540 °C-annealed alloy, the μi of about 10 000 at f = 10 kHz has no perceivable decline in this temperature range and can hold up to more than 400 °C. Such a magnetic softness at elevated temperature is superior to that of Finemet-type Fe-based nanocrystalline alloys ever reported. The origin of the high temperature magnetic softness was interpreted by the enhancement effect of Curie temperature in residual amorphous matrix. |
---|---|
ISSN: | 0021-8979 1089-7550 |
DOI: | 10.1063/1.4759243 |