Pyro and Kinetic Studies of Barium Oxalate Crystals Grown in Agar Gel

Single crystals of barium oxalate have been grown using gel method at ambient temperature. Thermal characteristics and kinetic parameters of barium oxalate crystals were determined by thermo-gravimetric (TG) analysis under non-isothermal heating conditions. The pyrolysis experiments were performed w...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of crystallization process and technology 2012-10, Vol.2 (4), p.156-160
Hauptverfasser: Dalal, Paresh V., Saraf, Kishor B., Shimpi, Navinchandra G., Shah, Navneet R.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Single crystals of barium oxalate have been grown using gel method at ambient temperature. Thermal characteristics and kinetic parameters of barium oxalate crystals were determined by thermo-gravimetric (TG) analysis under non-isothermal heating conditions. The pyrolysis experiments were performed with increasing temperature up-to 600 at heating rate of 5, 7 and 10 in nitrogen gas atmosphere. The pyrolysis curve showed that loss of mass took place mainly in the range of 220 - 400. At higher temperature there was a significant mass loss due to decomposition of oxalates. Ozawa and Coats & Redfern methods were used to determine the apparent activation energies of material degradation. The apparent activation energies for barium oxalate crystals were obtained 187.42 KJ.mol super(-1) and 185.4 KJ.mol super(-1) for the respective methods.
ISSN:2161-7678
2161-7686
DOI:10.4236/jcpt.2012.24023