Distorted colloidal crystal of similar-sized aggregates (1.5 μm in diameter) of nano-sized diamond particles (4 nm in diameter)

Distorted colloidal crystal suspension of similar-sized aggregates of diamonds (1.5 μm in diameter) was obtained by the deionization of aqueous suspension of the pre-particles of diamond, 4 nm in diameter. The stability, characteristics, and the rigidity of the crystal-like suspensions were studied. The main cause for the formation of the similar-sized aggregates is deduced to be the cooperation between the van de Waals inter-particle attraction and the repulsion induced by the vigorous thermal motion of the pre-particles. The rigidity was evaluated from the microscopic observation in the sedimentation equilibrium. Fluctuation parameters of the distorted colloidal crystals estimated from the rigidities were between 0.03 and 0.06, which are quite similar to those of typical colloidal crystals and solids of hard spheres.