Manufacture and demonstration of organic photovoltaic-powered electrochromic displays using roll coating methods and printable electrolytes

Electrochromic devices (ECDs) were prepared on flexible substrates using spray coating and slot‐die coating methods. The electrochromic materials were the conjugated electroactive polymers, poly((2,2‐bis(2‐ethylhexyloxymethyl)‐propylene‐1,3‐dioxy)‐3,4‐thiophene‐2,5‐diyl) as a vibrantly colored active material (ECP‐Magenta) and poly(N‐octadecyl‐(propylene‐1,3‐dioxy)‐3,4‐pyrrole‐2,5‐diyl) as a minimally colored, charge balancing material (MCCP). Two electrolyte systems were compared to allow development of fully printable and laminated devices on flexible substrates. Devices of various sizes, up to 7 × 8 cm2, are demonstrated with pixelated devices containing pixel sizes of 4 × 4 mm2 or 13 × 13 mm2. The transmission contrast exhibited by the devices, when switched between the fully bleached and fully colored state, was 58% at a visible wavelength of 550 nm, and the devices exhibited switching times of