Molecular Behavior of Room-temperature Ionic Liquids under Lubricating Condition

The molecular behavior of room-temperature ionic liquids (RTILs) under lubricating condition was analyzed using fourier transform infrared spectroscopy equipped with a pin-on-disk tribometer to simultaneously measure the friction force, normal load, and IR spectrum. When 1-metyl-3-butylimidazolium t...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Tribology letters 2013-08, Vol.51 (2), p.227-234
Hauptverfasser: Watanabe, Seiya, Takiwatari, Koji, Nakano, Miki, Miyake, Koji, Tsuboi, Ryo, Sasaki, Shinya
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The molecular behavior of room-temperature ionic liquids (RTILs) under lubricating condition was analyzed using fourier transform infrared spectroscopy equipped with a pin-on-disk tribometer to simultaneously measure the friction force, normal load, and IR spectrum. When 1-metyl-3-butylimidazolium trifluoromethanesulfonate ([BMIM]OTf), which is miscible with water, was used as a lubricant, the water content increased with time, and the ratio of water to cation remained constant even though the film thickness reduced under the lubricating condition at a load of ~25 N. When 1-metyl-3-butylimidazolium tetrafluorophosphate ([BMIM]PF 6 ), which is water-insoluble, was used as a lubricant, the water content was quite small and increased slightly with time, and the ratio of water to cation also remained constant even when a normal load of ~25 N was applied. The SUJ2 pin surface showed oxidative discoloration after the friction test using [BMIM]OTf, but there was little change in color when[BMIM]PF 6 was used. XPS results indicated that iron oxide, chromium oxide and sulfate were observed on the worn pin surface using [BMIM]OTf and the CaF 2 disk. However, iron oxide and iron phosphate were observed for the worn pin surface using [BMIM]PF 6 and the CaF 2 disk. These results suggest that the amount of water contained in the RTILs as well as window materials have a significant effect on the tribo-chemical reaction of RTILs.
ISSN:1023-8883
1573-2711
DOI:10.1007/s11249-013-0130-1