Tensile deformation and failure of North American porcupine quills

Although the mechanical properties of some keratin-based biological materials have been extensively studied (i.e., wool) and others are beginning to be studied (e.g., horn, hooves and avian quills), data on the properties of porcupine quill are less common. Porcupine quill is a keratin-based biological material composed of a cylindrical outer shell with an inner foam core. The present paper reports on the physical characteristics, tensile properties and fracture behavior of North American porcupine quills conditioned at relative humidities of 65% and 100%. Increasing the water content decreased the tensile stiffness and strength and increased the strain at fracture of the porcupine quills. The tensile fracture strength of porcupine quill was found to be 146 MPa at 65% RH and 60 MPa at 100% RH. Although these values compare favorably with reported values for African porcupine quill, reported values of the tensile strengths of wool with similar moisture contents are considerably higher. The initial moduli of porcupine quill (2700 MPa at 65% RH and 1000 MPa at 100% RH) compare favorably to those reported for wool but are considerably less than previous reports for African porcupine quill. The engineering strains at fracture were measured as 25% at 65% RH and 49% at 100% RH and these values are also comparable to other keratin-based mammalian materials. Scanning electron microscopy of the fracture surfaces of porcupine quills revealed that the cylindrical outer shells of quills are composed of 2–3 layers with distinctly different fracture characteristics, especially when the samples contain 100% RH. The outer layer of the porcupine quill shell appears to resist the plasticizing effects of moisture and appears to exhibit considerably less ductility than the inner layers, perhaps due to the presence of hydrophobic lipids in the outer layer. ► We characterize the tensile properties of north American porcupine quill. ► Elastic modulus, tensile strength and fracture strain depend upon moisture content. ► Fracture surfaces reveal differences in fracture behavior across the outer shell of the quills.