Measurement of the diffusivity of CdTe in liquid Te at crystal growth temperatures
The diffusivity of CdTe in tellurium-rich liquid solution was measured by dissolving solid samples at temperatures applicable to THM crystal growth. We calculated the resulting diffusion coefficients to be 0.008mm2/s at 850°C and 0.009mm2/s at 900°C. The CdTe was dissolved under isothermal condition...
Gespeichert in:
Veröffentlicht in: | Journal of crystal growth 2015-02, Vol.411, p.30-33 |
---|---|
Hauptverfasser: | , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The diffusivity of CdTe in tellurium-rich liquid solution was measured by dissolving solid samples at temperatures applicable to THM crystal growth. We calculated the resulting diffusion coefficients to be 0.008mm2/s at 850°C and 0.009mm2/s at 900°C. The CdTe was dissolved under isothermal conditions in 7mm diameter quartz tubes for 45min, 90min and 180min. The diffusivity was calculated from the distance travelled by the dissolution interface using a 1D transport model. Measurement of the solution composition by EDS confirms that the experiments were diffusion-dominated, and the calculated diffusivities match those predicted elsewhere ab initio for similar conditions.
•We dissolved CdTe in tellurium under isothermal conditions at 850°C and 900°C.•The diffusivity of CdTe in Te was measured to be 0.008mm2/s at 850°C and 0.009mm2/s at 900°C.•An analytical 1D model was used to calculate the diffusivity.•Measurement of the composition of the quenched solution by EDS confirms that transport in the system was diffusion-dominated. |
---|---|