A Novel Bonding Method of Pure Aluminum and SUS304 Stainless Steel Using Barrel Nitriding

A great deal of research is being carried out on welding or bonding methods between iron and aluminum. However, it is not so easy to make Fe-Al bonding materials with both high strength and light weight. Recently, a new nitriding process has been proposed to produce aluminum nitride on an aluminum surface using a barrel. This study proposes a new concept in the production of a multilayer which has an AlN and Fe-Al intermetallic compound layer between the aluminum and steel using a barrel nitriding process. The bonding process was carried out from 893 K to 913 K (620 °C to 640 °C) for 18, 25.2, and 36 ks with Al 2 O 3 powder and Al-Mg alloy powder. After the process, an aluminum nitride (AlN) layer and a Fe-Al intermetallic compound (Fe 2 Al 5.4 ) layer were formed at the interface between the pure aluminum and SUS304 austenitic stainless steel. The thicknesses of the AlN layer and the intermetallic compound layer increased with increasing treatment temperature and time. The maximum hardnesses of the AlN layer and Fe 2 Al 5.4 layers were found to be 377HV and 910HV, respectively, after barrel nitriding at 893 K (620 °C) for 18 ks.