Nanomechanical Properties and Surface Wettability of Carbon Films Prepared by Magnetron Sputtering

In this work, carbon films were deposited by magnetron sputtering on silicon substrate. The effect of sputtering time on the surface wettability and mechanical properties of carbon films was investigated. Contact angle measurement was used to analyse surface wettability, and the nanomechanical prope...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Key engineering materials 2014-04, Vol.609-610, p.357-361
Hauptverfasser: Gu, Le, An, Wei Wei, Su, Run Zhou, Zhao, Xiao Li
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In this work, carbon films were deposited by magnetron sputtering on silicon substrate. The effect of sputtering time on the surface wettability and mechanical properties of carbon films was investigated. Contact angle measurement was used to analyse surface wettability, and the nanomechanical properties were characterized by nanoindentation. In experiments, the sputtering time was 45 min, 60 min, 75 min and 90 min. The measurement results show that the maximum film hardness was achieved for sputtering time 90 min, with a value of 2.34 GPa. Longer sputtering time resulted in preferable mechanical properties. It was analyzed that the size of the crystal grains on the substrate surface and thickness of the films were increased with the increment of sputtering time. The surface roughness decreased with the increase of sputtering time. Moreover, Youngs modulus increased with sputtering time and the maximum value was 16.94 GPa. The contact angle measurement results show that the prepared films take on the hydrophilicity. The minimum contact angle was achieved for sputtering time 45 min with a value of 54o.
ISSN:1013-9826
1662-9795
1662-9795
DOI:10.4028/www.scientific.net/KEM.609-610.357