Study of Geopolymeric Binders of Fly Ash/Meta kaolin Mixtures Cured at Room Temperature

Geopolymerization is a chemical process in which aluminosilicate materials are precursors to obtain binders that have a low environmental impact. Fly ash has been used as a precursor for the development of these binders. However, thermal curing is needed to accelerate the polycondensation of aluminosilicate, which limits the application of this new binder in the construction industry. Thus, the objective of this study was to evaluate the feasibility to obtain such binders with good mechanical properties when cured at room temperature. The precursor material consisted of different mixtures of fly ash and meta kaolin that were activated using combined sodium hydroxide and sodium silicate alkaline solutions. The effect on the compressive strength of different proportions of the alkaline solutions was studied. Compressive strengths of about 40 MPa were achieved at 91 days for the samples containing 70% fly ash and 30% meta kaolin, activated using an alkaline solution of 50% sodium hydroxide and 50% sodium silicate. X-ray diffraction analysis showed the formation of natrite in geopolymeric samples, as well as the presence of crystalline compounds, such as quartz, mullite and hematite, in fly ash and meta kaoline. Scanning electron microscopy analysis showed that in geopolymeric mixtures with higher compressive strength dissolution of fly ash and metakaolin particles occurred almost completely and that aluminosilicate dense gel has been formed extensively.