The effects of silane-SiO2 nanocomposite films on Candida albicans adhesion and the surface and physical properties of acrylic resin denture base material

Statement of problem Polysiloxane has been used as a coupling material in restorative dental materials for several decades. However, few studies are available on the application of polysiloxane in other dental prosthesis functions. Purpose The purpose of this study was to investigate the effects of silane-SiO2 nanocomposite films on Candida albicans adhesion and the surface and physical properties of acrylic resin denture base materials. Material and methods Specimens were separated into 2 groups, uncoated and coated. They were coated with a film by using the dip-coating method. Specimens were incubated with Candida albicans 107 cells/mL for 1 hour, and the adherent cells were counted under an optical microscope. The following surface properties were measured: surface chemical composition with Fourier-transform infrared spectrometry, surface roughness with a surface profiler, surface energy with the sessile drop method, and surface hardness with a microhardness tester. The physical properties, including water sorption, water solubility, ultimate flexural strength, and flexural modulus, were evaluated according to International Organization for Standardization 20795-1 requirements. The adhesion of Candida albicans and the surface properties of the specimens were investigated after cleaning with effervescent tablets and brushing. An MTT assay was used to evaluate the coated specimens. The results were statistically analyzed with the Mann-Whitney U test (α=.05). Results A significant reduction in Candida albicans adhesion ( P =.002) was observed before cleaning. In addition, the surface energy was comparable ( P =.100), the surface hardness increased significantly ( P =.008), and the surface roughness remained unchanged ( P =.310). After cleaning with effervescent tablets, a significant decrease in Candida albicans adhesion ( P =.002) and in surface roughness ( P =.008) was observed; however, similar surface energies were measured ( P =.100). After cleaning with a toothbrush, the adhesion of Candida albicans was significantly higher on the coated specimen than on the uncoated specimen ( P =.004). The surface roughness values were significantly different ( P =.008), and the surface energies could not be determined. The coated specimen had a silicon-oxygen-silicon peak instead of an ester bond in the polymethyl methacrylate structure. The coating film reduced the water sorption ( P =.008) and water solubility ( P =.032), and increased the ultimate flexural stre