Korrosionsverhalten metallischer Werkstoffe fuer innovative Vergasungsverfahren

Metallic materials for highly stressed oxygen nozzles and recovery boilers were studied in respect to their corrosion resistance in H sub(2)/H sub(2)O/H sub(2)S laboratory test gas. Screening tests using ferritic and austenitic steels and nickel-base alloys were carried out and from the results promising alloys selected and tested at various temperatures. With one exception, all alloys show bell-shape temperature dependence of the oxidation kinetics. Results from studies on model alloys will be used to derive optimised alloy compositions which exhibit protective oxide scale formation in the whole temperature range considered in the present studies.Original Abstract: Metallische Werkstoffe fuer hochbeanspruchte Sauerstoffduesen und Abhitzekessel wurden auf ihre Korrosionsbestaendigkeit in einem H sub(2)/H sub(2)O/H sub(2)S-Laborgas untersucht. In Screening-Versuchen an ferritischen und austenitischen Staehlen und Nickelbasislegierungen wurden vielversprechende Legierungen ermittelt. Fuer alle untersuchten Werkstoffe, mit einer Ausnahme, ergab sich eine Bell-Shape-Abhaengigkeit der Oxidationskinetik. Durch Untersuchungen an Modelllegierungen wird die Wirkung einzelner Legierungselemente auf die Korrosionsmechanismen ermittelt, um hieraus optimierte Legierungszusammensetzungen herzuleiten.