Evidence for the intrinsic nature of band-gap states electrochemically observed on atomically flat TiO2(110) surfaces
Using an ultra-high vacuum (UHV) electrochemistry approach with pulsed laser deposition (PLD), we investigated the band-gap state for TiO2(110). In the PLD chamber, a TiO2(110) surface was cleaned by annealing in O2 enough for it to exhibit a sharp (1 × 1) reflection high energy electron diffraction...
Gespeichert in:
Veröffentlicht in: | Physical chemistry chemical physics : PCCP 2014-12, Vol.16 (45), p.24784-24789 |
---|---|
Hauptverfasser: | , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Using an ultra-high vacuum (UHV) electrochemistry approach with pulsed laser deposition (PLD), we investigated the band-gap state for TiO2(110). In the PLD chamber, a TiO2(110) surface was cleaned by annealing in O2 enough for it to exhibit a sharp (1 × 1) reflection high energy electron diffraction (RHEED) pattern. The cleaned TiO2(110)-(1 × 1) sample then underwent electrochemical measurements without exposure to air, showing the band-gap state at -0.14 V vs. Ag by Mott-Schottky plot analysis. The band-gap state gradually disappeared under UV illumination at +0.6 V vs. Ag due to photoetching, and reappeared on reduction in a vacuum and/or deposition of a fresh TiO2 film. These results indicated that the electrochemically observed band-gap state for TiO2(110) was a defect state due to oxygen deficiency, most probably identical to that observed under UHV, which does not necessarily exist on the surface. A quantitative analysis of the defect density suggests that the origin of this defect state is not the surface bridging hydroxyls or oxygen vacancies, but rather the interstitial Ti(3+) ions in the subsurface region. |
---|---|
ISSN: | 1463-9084 |
DOI: | 10.1039/c4cp03280b |