Trends of Parallel Microstructure and Magnetic Properties Evolution in Co sub(0.5)Zn sub(0.5)Fe sub(2)O sub(4)

The present paper reports on an effort to expose and scientifically explain the microstructure-magnetic properties relationship as they evolve with increasing sintering temperature. Mechanical alloying was used to prepare cobalt-zinc ferrite nanoparticles with sintering temperature from 800 to 1,350 degree C with 50 degree C increment. The microstructure of the samples was observed using a field emission scanning electron microscope, and the magnetic parameters, such as the real permeability and loss factor, were measured at room temperature in the frequency range from 10 MHz to 1.0 GHz using an Agilent 4291B impedance/material analyzer. The B-H hysteresis of the samples was investigated using a MATS-2010SD Static Hysteresisgraph. From the results, the real permeability and loss factor were observed to increase up to 1,250 degree C. These increases corresponded to increases in grain size and are mainly due to easier domain wall movement. However, due to zinc loss, \(\mu \prime }\) and \(\mu \prime \prime }\) as well as the saturation induction decreased from 1,300 to 1,350 degree C. The coercivity increased up to 850 degree C and decreased with increasing temperature. This increasing-to-decreasing coercivity trend corresponded well with the single- to multi-domain grain size transition marked by critical grain size at about 0.13 mu m.